- Tytuł:
- Spark Plasma Sintering of Mn-Zn Ferrite Powders by High Energy Ball Milling
- Autorzy:
-
Suh, Jun Young
Song, Yo-Seung
Chang, Si Young - Tematy:
-
high energy ball milling
nano-sized particles
SPS
conventional sintering
density - Pokaż więcej
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Powiązania:
- https://bibliotekanauki.pl/articles/351276.pdf Link otwiera się w nowym oknie
- Opis:
- The Mn-Zn ferrite powders prepared by high energy ball milling were heat-treated, subsequently compacted and sintered by spark plasma sintering (SPS). Based on the observation of microstructure, the characteristics of samples after SPS were investigated and compared with ones after conventional sintering. The size of initial powders was approximately 650 nm and decreased to 230 nm after milling at 300 rpm for 3 h. After heat treatment at 973 K for 1 h, the milled powders became larger to approximately 550 nm in size again and the peaks of Mn2 O3 disappeared in XRD patterns. In the samples after SPS, the Fe2 O3 and MnZnFe2 O4 phases decomposed at the higher temperatures than 1173 K and 1373 K, respectively, while only MnZnFe2 O4 phase was detected in the samples conventionally sintered at 1273~1673 K. As the sintering temperature increased, the relative density after SPS increased more quickly than that after conventional sintering. In particular, it reached approximately 99% after SPS at 1473 K.
- Dostawca treści:
- Biblioteka Nauki
Artykuł