Temat: intermetallic coating

Skocz do pozycji: 1.

Tytuł:: Effect of Isothermal Treatment on Ni3Al Coatings Deposited by Air Plasma Spraying System
Autorzy:: Mehmood, K.
Rafiq, M. A.
Durrani, Y. A.
Khan, A. N.
Tematy:: air plasma spraying
Ni-20Al
residual stresses
intermetallic coating
nickel aluminide; Pokaż więcej
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Powiązania:: https://bibliotekanauki.pl/articles/354178.pdf Link otwiera się w nowym oknie
Opis:: Ni₃Al coatings were obtained on AISI 321 steel samples by air plasma spraying system. The behavior of heat treatment on intermetallic coatings were evaluated after exposure at various temperatures i.e. 500ºC to 800ºC. The stay time in this regard was varied from 10 to 100 hours. The coatings were then characterized by X-Ray diffraction analysis, optical and scanning electron microscopy, eddy current measurements and stress analysis. It was observed that the formation of NiO increases drastically with time and temperature. The hardness of the coating increases with the formation of NiO. It was noted that the residual stresses can be correlated with the formation of NiO. Further, the development of residual stresses can be monitored by a non-destructive technique i.e. eddy current method.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 2.

Tytuł:: Tribological wear of Fe-Al coatings applied by gas detonation spraying
Autorzy:: Chrostek, Tomasz
Tematy:: gas detonation spraying
GDS
coating
Fe-Al
intermetallic alloys
tribology; Pokaż więcej
Wydawca:: Uniwersytet Warmińsko-Mazurski w Olsztynie
Powiązania:: https://bibliotekanauki.pl/articles/2069744.pdf Link otwiera się w nowym oknie
Opis:: Comparative tests of gas detonation (GDS) coatings were carried out in order to investigate the influence of spraying parameters on abrasive wear under dry friction conditions. The tests were carried out using the pin-on-disc (PoD) method at room temperature. The microstructure of the coatings was analysed by X-ray diffraction (XRD) and scanning electron microscopy (SEM/EDS) methods. The results showed that with certain parameters of the GDS process, the main phase of the produced coatings is the FeAl phase with the participation of thin oxide layers, mainly Al2O3. The tribological tests proved that the coatings sprayed with the shorter barrel of the GDS gun showed higher wear resistance. The coefficient of friction was slightly lower in the case of coatings sprayed with the longer barrel of the GDS gun. During dry friction, oxide layers form on the surface, which act as a solid lubricant. The load applied to the samples during the tests causes shear stresses, thus increasing the wear of the coatings. During friction, the surface of the coatings is subjected to alternating tensile and compressive stresses, which lead to delamination and is the main wear mechanism of the coatings.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 3.

Tytuł:: Fabrication and Microstructure of Diffusion Alloyed Layers on Pure Magnesium Substrate
Wytwarzanie i struktura dyfuzyjnych stopowych warstw na magnezie
Autorzy:: Mola, R.
Tematy:: magnesium
alloyed coating
Mg-Al-Zn intermetallic phases
hardness
magnez
warstwy stopowe
fazy międzymetaliczne Mg-Al-Zn
twardość; Pokaż więcej
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Powiązania:: https://bibliotekanauki.pl/articles/352037.pdf Link otwiera się w nowym oknie
Opis:: Alloyed layers on pure magnesium were created by means of the heating of the magnesium sample covered with Al+Zn powders mixture containing 20 wt.% Zn and 40 wt.% Zn in vacuum furnace. The microstructure and related composition of the alloyed layers were investigated using optical microscopy and scanning electron microscopy equipped with an energy dispersive X-ray system (EDS). The results revealed that the microstructure, thickness and microhardness of the obtained layers depended on the Zn content in the powder mixture. The alloyed layers were composed of the Mg-Al-Zn intermetallic phases and Mg-based solid solution containing Al and Zn. The multi-phase layer was diffusion bonded with magnesium substrate. The thickness of the layer fabricated by the heat treatment in contact with a powder mixture containing 40 wt.% Zn was twice as high as compared to that obtained with the powder mixture containing 20 wt.% Zn. The hardness value of the alloyed layers was much higher than that of the magnesium substrate.
Warstwy stopowe na magnezie zostały wytworzone poprzez wygrzewanie próbek w kontakcie z mieszankami proszków Al+Zn zawierajacymi 20% mas. Zn i 40% mas. Zn w piecu próżniowym (oznaczone jako: Al20Zn i Al40Zn). Badania struktury i składu chemicznego przeprowadzono na mikroskopie optycznym oraz elektronowym mikroskopie skaningowym wyposażonym w mikroanalizator rentgenowski. Wyniki badań wykazały, że mikrostruktura, grubość oraz mikrotwardość otrzymanych warstw zależą od zawartości Zn w mieszankach proszków. Warstwy stopowe składały się z faz międzymetalicznych Mg-Al-Zn i roztworu stałego Al i Zn w Mg i były dyfuzyjnie połączone z podłożem-magnezem. Grubość warstwy wytworzonej na podłożu magnezowym poprzez wygrzewanie próbek w kontakcie z mieszanką proszków zawierającą 40% mas. Zn była dwa razy większa w porównaniu do warstwy otrzymanej w mieszance zawierającej 20% mas. Zn. Twardość otrzymanych warstw stopowych była znacznie wyższa w porównaniu do twardości podłoża.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Informacja

Wyszukujesz frazę "intermetallic coating" wg kryterium: Temat