Temat: titanium coating - Prolib Integro

Skocz do pozycji: 1.

Tytuł:: Titanium metallization coating deposited on AlN ceramics substrate by means of friction surfacing process
Tytanowa powłoka metalizacyjna osadzona na powierzchni ceramiki AlN metodą tarciową
Autorzy:: Hudycz, Michał
Tematy:: metalizacja
napawanie tarciowe
powłoka tytanowa
metallization
friction surfacing
titanium coating; Pokaż więcej
Wydawca:: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
Powiązania:: https://bibliotekanauki.pl/articles/115026.pdf Link otwiera się w nowym oknie
Opis:: The article characterizes a titanium metallization coating frictionally deposited on the surface of AlN ceramics. The method of preparing materials for metallization and the idea of the process were described. The results of stereometric tests of coating surfaces, metallographic tests and phase analysis are presented. Tests were carried out on the adhesion of the coating to the substrate and brazing tests of metallized ceramics with an FeNi42 alloy in an argon sheath using AgCu28 eutectic solder.
W artykule scharakteryzowano metalizacyjną powłokę tytanową osadzoną tarciowo na powierzchni ceramiki AlN. Opisano sposób przygotowania materiałów do metalizacji oraz ideę procesu. Przedstawiono wyniki badań stereometrycznych powierzchni nakładanych powłok, badań metalograficznych, analizy fazowej. Wykonano próby przyczepności powłoki do podłoża i próby lutowania metalizowanej ceramiki ze stopem FeNi42 w osłonie argonu za pomocą eutektycznego lutu AgCu28.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 2.

Tytuł:: Indentation testing of thin titanium coatings sprayed with cold gas
Autorzy:: Makrenek, M.
Żórawski, W.
Tematy:: natryskiwanie cieplne
powłoka tytanowa
nanotwardość
thermal spraying
titanium coating
nanohardness; Pokaż więcej
Wydawca:: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
Powiązania:: https://bibliotekanauki.pl/articles/115202.pdf Link otwiera się w nowym oknie
Opis:: Material hardness is one of the basic parameters characterizing the properties of matter. In the nanohardness studies, the intendant’s deformation can not be neglected. Assuming the proportionality of the intender’s deformation to the hardness of the material being tested, a relative hardness measurement was used in the work. Hardness measurement was carried out for fused silica, which was a reference sample. With the same nanotesting parameters, a nanoscale measurement was carried out for two samples.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 3.

Tytuł:: Formation of Surface Topography During Turning of AISI 1045 Steel Considering the Type of Cutting Edge Coating
Autorzy:: Szczotkarz, Natalia
Maruda, Radosław W.
Dębowski, Daniel
Leksycki, Kamil
Wojciechowski, Szymon
Khanna, Navneet
Królczyk, Grzegorz M.
Tematy:: turning
surface topography
dry machining
titanium coating
AISI 1045 steel
toczenie
topografia powierzchni
obróbka na sucho
powłoka tytanowa
stal AISI 1045; Pokaż więcej
Wydawca:: Stowarzyszenie Inżynierów i Techników Mechaników Polskich
Powiązania:: https://bibliotekanauki.pl/articles/2023489.pdf Link otwiera się w nowym oknie
Opis:: The paper presents evaluation of the surface topography obtained after turning of AISI 1045 steel with the use of cemented carbide tools diversified in terms of applied titanium-based coatings. During the research, three types of coatings deposited with the PVD method on a P25 sintered carbide insert were compared: nitride-titanium TiN, nitride-aluminum-titanium TiAlN and carbon-titanium TiC in a wide range of variable cutting speeds 125 - 325 m/min and variable feeds 0.05 - 0.25 mm/rev. The quality of the machined surface was assessed on the Sensofar S neox System optical profile meter using the confocal method. The paper presents the results of 3D parameters, contour maps, isometric views and material ratio curves. The surface topography analysis showed that for the TiAlN coated insert, lower surface roughness parameters were observed in the range of lower cutting speeds and higher feeds, while for higher cutting speeds, lower values of the selected 3D parameters were found for the insert with TiC coating. For the insert with TiC coating, the most even distribution of the valleys and ridges of the machined surface roughness was also observed. The research results determined the range of cutting parameters that allow the selection of the appropriate type of titanium-based coating when machining AISI 1045 steel.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 4.

Tytuł:: Morfologia powłok TiCN nanoszonych techniką fizycznego osadzania z fazy gazowej (PVD)
Morphology of TiCN coating deposited by physical vapour deposition technique
Autorzy:: Madej, M.
Ozimina, D.
Kowalczyk, J.
Pawelec, K.
Tematy:: titanium nitride-carbide coating
TiCN coating morphology
cutting tool
azotek tytanu
morfologia powłoki
narzędzia tnące
TiCN; Pokaż więcej
Wydawca:: Wydawnictwo AWART
Powiązania:: https://bibliotekanauki.pl/articles/404424.pdf Link otwiera się w nowym oknie
Opis:: In this paper the results of researches of coatings TiCN morphology were presented. Tested coating were deposited by PVD technique on tool steel HS6-5-2C surface. Coating thickness were measured by means of compact device Calotest CATs and optical microscope. Coating structure and its chemical analysis were made with the aid of electron microscope JSM 7100F with analyzer EDS. Hardness of coating were measured with the aid of hardness tester INNOVATEST. On the base of investigations results it was found that morphology features of tested coating fulfil potential requirements, e.g. on cutting tool edges or on machine elements worked in rugged conditions (great load, high temperature).
W artykule przedstawiono wyniki badań dotyczących morfologii powłok węglikoazotku tytanu TiCN uzyskanych w procesie fizycznego osadzania z fazy gazowej PVD na stali narzędziowej HS6-5-2C. Pomiaru grubości powłoki dokonano przy użyciu kompaktowego urządzenia Calotest CATc oraz mikroskopu optycznego. Obserwacje struktury i analizę składu chemicznego wykonano skaningowym mikroskopem elektronowym JSM 7100F wyposażonym w analizator EDS. Twardość zmierzono twardościomierzem INNOVATEST. Na podstawie rezultatów badań stwierdzono, że cechy morfologiczne badanych powłok spełniają potrzeby wynikające z ich potencjalnych zastosowań, a więc na ostrzach narzędzi skrawających i na elementach pracujących w trudnych warunkach (duże obciążenie, wysoka temperatura).
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 5.

Tytuł:: Porous SiO2/HAp Coatings on Cp-Titanium Grade 1 Surfaces Produced by Electrophoretic Deposition
Autorzy:: Moskalewicz, T.
Babkiewicz, A.
Dubiel, B.
Kot, M.
Radziszewska, A.
Łukaszczyk, A.
Tematy:: titanium
porous coating
corrosion resistance
electrophoretic deposition; Pokaż więcej
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Powiązania:: https://bibliotekanauki.pl/articles/356668.pdf Link otwiera się w nowym oknie
Opis:: Porous hydroxyapatite doped SiO₂ coatings were electrophoretically deposited (EPD) on commercially pure titanium. The influence of EPD parameters on coatings quality was investigated. Microstructural observation was done using transmission and scanning electron microscopy as well as X-ray diffractometry. The coatings consisted of spherical micro and nanocrystalline hydroxyapatite (HAp) as well as amorphous SiO₂ nanoparticles. The coatings exhibited open porosity with pore diameter up to 1 μm and due to presence of nanoparticles high surface development. It was found that application of SiO₂/HAp coating increase corrosion resistance of titanium in Ringer’s solution.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 6.

Tytuł:: Improvement of the Properties of Ti6Al7Nb Titanium Alloy in Terms of the Type of Surface Modification
Autorzy:: Woźniak, A.
Bialas, O.
Adamiak, M.
Tematy:: titanium alloys
sol-gel method
ZrO2 coating
EIS
AFM; Pokaż więcej
Wydawca:: Polska Akademia Nauk. Czytelnia Czasopism PAN
Powiązania:: https://bibliotekanauki.pl/articles/353294.pdf Link otwiera się w nowym oknie
Opis:: The paper presents the influence of ZrO₂ coating on Ti6Al7Nb titanium alloy depending on the method of deposition. The coatings were made by sol-gel method and atomic layer deposition (ALD). Wettability tests, pitting corrosion assessment and electrochemical impedance spectroscopy (EIS) were carried out in the paper. Complementary macro- and microscopic observations, roughness analysis by profilometric method and atomic force microscopy (AFM) were made. Based on the results obtained, it can be concluded that the type of method of depositing the layer on the surface of the material has a significant influence on its properties and that it should be taken into account during the process of the material improvement. Drawing on the findings presented, it can be inferred that roughness has a significant impact upon the surface wetttability of the tested surfaces and their related corrosion resistance. The obtainment of hydrophobic surfaces is for smaller rougidity values.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 7.

Tytuł:: Kompozytowa powłoka PEEK /Bioszkło® na stopie tytanu Ti-6Al-7Nb do zastosowań w medycynie
Composite polyetheretherketone/ Bioglass® coating on Ti-6Al-7Nb alloy for medical application
Autorzy:: Moskalewicz, T.
Seuss, S.
Boccaccini, A. R.
Kot, M.
Czyrska-Filemonowicz, A.
Tematy:: stop tytanu
powłoka kompozytowa
PEEK
bioszkło
titanium alloy
composite coating
bioglass; Pokaż więcej
Wydawca:: Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów
Powiązania:: https://bibliotekanauki.pl/articles/284982.pdf Link otwiera się w nowym oknie
Opis:: Kompozytową powłokę polieteroeteroketon (PEEK)/ Bioszkło osadzono metodą elektroforezy na stopie tytanu Ti-6Al-7Nb. W celu poprawy przyczepności powłoki do podłoża próbkę poddano wyżarzaniu po obróbce powierzchniowej. Mikrostrukturę powłoki charakteryzowano za pomocą mikroskopii świetlnej oraz skaningowej- i transmisyjnej mikroskopii elektronowej. Powłoka była jednorodna i porowata, nie stwierdzono obecności pęknięć. Powłoka zbudowana była z cząstek bioszkła rozmieszczonych w polimerowej osnowie. Wyniki liniowej analizy składu chemicznego wykonanej metodą STEM-EDS wskazują na dyfuzję Na ze szkła do polimeru podczas wygrzewania próbki.
A composite polyetheretherketone (PEEK)/Bioglass® coating was electrophoretically deposited on the Ti-6Al-7Nb substrate. Post heat treatment was performed to improve the adhesion of the coating to the substrate. The microstructure of the coating and a substrate was examined by light microscopy, scanning- and transmission electron microscopy methods. The coating is uniformly porous, without any cracks or presence of large voids. The coating is composed of Bioglass® particles embedded in a PEEK matrix. STEM-EDS line analysis revealed diffusion of Na from the glass to the PEEK.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 8.

Tytuł:: Investigating the Effects of PU-Based Back-Coating with Boric Acid and Titanium Dioxide Additives on Flame Retardancy Levels and Comfort Properties of 100% Cotton Denim Fabric
Autorzy:: Öztürkmen, Ebru
Güneşoğlu, Cem
Topalbekiroğlu, Mehmet
Tematy:: flame retardant
thermophysiological comfort
back coating
denim fabric
boric acid
titanium dioxide; Pokaż więcej
Wydawca:: Sieć Badawcza Łukasiewicz - Instytut Biopolimerów i Włókien Chemicznych
Powiązania:: https://bibliotekanauki.pl/articles/59115106.pdf Link otwiera się w nowym oknie
Opis:: This study aimed to develop a cost-effective and resource-efficient application to enhance the thermal stability, flame retardancy, self-cleaning, and antibacterial properties of cotton denim fabrics through a single-step, flexible, and simple polyurethane (PU) based back-coating method, ultimately increasing the use of denim fabrics in daily and work clothes thanks to the increased functionality. This method utilizes boric acid (H3BO3) and a binary composite of H3BO3-titanium dioxide (TiO2) as functional additives while considering comfort parameters. Limiting oxygen index (LOI) and vertical burning tests were conducted to explore the thermal stability and flame retardancy of the samples, while assessments of air permeability, water vapour permeability, thermal resistance, and thermal absorptivity were performed to investigate the comfort properties. Comparing two kinds of back-coated denim fabrics, H3BO3-TiO2 back-coated cotton fabric showed the best flame retardancy with the lowest char length (45 mm) and highest LOI (27%). The air permeability values of back-coated fabrics decreased by approximately half compared to the untreated denim fabric. Although the water vapour permeability values decreased, they were less affected by the coating. Coating application reduced thermal conductivity and thermal absorbency, resulting in more thermally resistant denim fabric. This study demonstrates the potential utility of a PU-based coating incorporating TiO2 and H3BO3 on traditional cotton denim fabrics to enhance flame resistance while minimizing any adverse effects on the overall thermal comfort of the fabric.
Dostawca treści:: Biblioteka Nauki

Artykuł

na półce

Skocz do pozycji: 9.

Tytuł:: Investigating the Effects of PU-Based Back-Coating with Boric Acid and Titanium Dioxide Additives on Flame Retardancy Levels and Comfort Properties of 100% Cotton Denim Fabric
Autorzy:: Topalbekiroğlu, Mehmet
Maciej Boguń
Güneşoğlu, Cem
Öztürkmen, Ebru
Współwytwórcy:: Maciej Boguń
Wydawca:: Sciendo
Cytata wydawnicza:: Öztürkmen, E., Güneşoğlu, C. & Topalbekiroğlu, M. Investigating the Effects of PU-Based Back-Coating with Boric Acid and Titanium Dioxide Additives on Flame Retardancy Levels and Comfort Properties of 100% Cotton Denim Fabric. Fibres & Textiles in Eastern Europe, 2024, Sciendo, vol. 32 no. 4, pp. 13-21. https://doi.org/10.2478/ftee-2024-0027
Opis:: This study aimed to develop a cost-effective and resource-efficient application to enhance the thermal stability, flame retardancy, self-cleaning, and antibacterial properties of cotton denim fabrics through a single-step, flexible, and simple polyurethane (PU) based back-coating method, ultimately increasing the use of denim fabrics in daily and work clothes thanks to the increased functionality. This method utilizes boric acid (H3BO3) and a binary composite of H3BO3-titanium dioxide (TiO2) as functional additives while considering comfort parameters. Limiting oxygen index (LOI) and vertical burning tests were conducted to explore the thermal stability and flame retardancy of the samples, while assessments of air permeability, water vapour permeability, thermal resistance, and thermal absorptivity were performed to investigate the comfort properties. Comparing two kinds of back-coated denim fabrics, H3BO3-TiO2 back-coated cotton fabric showed the best flame retardancy with the lowest char length (45 mm) and highest LOI (27%). The air permeability values of back-coated fabrics decreased by approximately half compared to the untreated denim fabric. Although the water vapour permeability values decreased, they were less affected by the coating. Coating application reduced thermal conductivity and thermal absorbency, resulting in more thermally resistant denim fabric. This study demonstrates the potential utility of a PU-based coating incorporating TiO2 and H3BO3 on traditional cotton denim fabrics to enhance flame resistance while minimizing any adverse effects on the overall thermal comfort of the fabric.
Dostawca treści:: Repozytorium Centrum Otwartej Nauki

Artykuł

na półce

Skocz do pozycji: 10.

Tytuł:: AFM-IR mapping of Escherichia coli disruption on silver nanoparticle-coated titanium : dual-function surfaces for antibacterial implants
Autorzy:: Piergies, Natalia
Chrabąszcz, Karolina
Święch, Dominika
Kozieł, Joanna
Palumbo, Gaetano
Golda, Anna
Oćwieja, Magdalena
Dostawca treści:: Repozytorium Uniwersytetu Jagiellońskiego

Artykuł

na półce

Informacja

Wyszukujesz frazę "titanium coating" wg kryterium: Temat