- Tytuł:
- Preparation of Twinned Dendrites of Al-Zn Alloy with High Zn Content
- Autorzy:
-
Gao, K.
Song, W.
Fan, L.
Ding, Y.
Guo, X.
Zhang, R. - Tematy:
-
directional solidification
twinned dendrite
microstructure
growth orientation
deviation angle - Pokaż więcej
- Wydawca:
- Polska Akademia Nauk. Czytelnia Czasopism PAN
- Powiązania:
- https://bibliotekanauki.pl/articles/351396.pdf Link otwiera się w nowym oknie
- Opis:
- Twinned dendrites in Al-Zn alloy with high Zn content (40% wt.%) were successfully prepared by directional solidification. At different directional solidification rates (1000 and 1500 μm/s), microstructures and growth orientation variations of Al twinned dendrite and non-twinned dendrite were characterized. By using the inverted trapezoidal graphite sleeve at 1000 μm/s, Al twinned dendrite were formed to developed feather crystal structures in longitudinal section. Its primary and secondary twinned dendrite were grew along [110] direction. Moreover the deviation angle between [110] direction of Al twinned dendrite and the heat flow direction was about 27.15°. While not using the inverted trapezoidal graphite sleeve at 1000 and 1500 μm/s, Al dendrite was the non-twinned dendrite and the twinned dendrite was not appeared. The experimental results showed that the higher temperature gradient, a certain pulling rate and convection environment were the formation conditions of twinned dendrites.
- Dostawca treści:
- Biblioteka Nauki
Artykuł